Versatile and Attractive Looks for Designer Creations Plexiglas G P-95 Plexiglas G DP-95 CELL-CAST ACRYLIC SHEET Added texture for decorative effects. n Premium-grade cell-cast sheet Specifically created for designers who manufacture POP n Distinct matte finish diffuses surface reflections and hides imperfections displays showcases signage and decorative furnishings Plexiglas G P-95 acrylic sheet and Plexiglas G DP-95 acrylic sheet provides a distinctive matte finish that effectively complements your product. This versatile material has many n Resists fingerprints scratches and smudges n Lightweight and weather resistant residential commercial industrial and professional uses. Sheets can be fabricated without altering the optical or COLOR OFFERING mechanical properties of the product. Plexiglas G P-95 and Plexiglas G DP-95 acrylic sheet are This high performance cell-cast material is available with the matte finish on either one side Plexiglas G P-95 or both sides Plexiglas G DP-95 of the sheet. available in more than 50 different colors including 3063 BlackWhite which is a specially formulated DayNight color as well as 3143 Infrared Transmitting Sheet. Visit our chips gallery at www.plexiglas.comgallery to see our wide range of color offerings. Plexiglas G P-95 Plexiglas G DP-95 CELL-CAST ACRYLIC SHEET TYPICAL STANDARD PROPERTIES PROPERTIES TEST METHOD UNITS VALUE in 0.236 Specific Gravity ASTM D-792 1.19 Rockwell Hardness ASTM D-785 M scale 100 Refractive Index ND 73F ASTM D-542 1.49 Luminous Transmittance1 ASTM D-1003 82.0 min Tensile Strength maximum ASTM D-638 psi 10500 Tensile Strength yield ASTM D-638 psi 10500 Tensile Elongation ASTM D-638 4.9 Tensile Modulus of Elasticity ASTM D-638 psi 450000 Flexural Strength maximum ASTM D-790 psi 16000 Flexural Modulus of Elasticity ASTM D-790 psi 450000 Shear Strength yield1 ASTM D-732 psi 9000 Shear Modulus ASTM D-732 psi 167000 Notched Izod impact 73F 23C ASTM D-256 ft-lb in 0.3 Un-notched Charpy 73F 23C A
STM D-256 ft-lb 0.5 x 1 section 7.0 Physical Nominal Thickness for data unless otherwise noted Optical Mechanical Thermal Deflection Temperature Under Flexural Load 264psi unannealed1 ASTM D-648 F 205 Coefficient of Thermal Expansion at 60F ASTM E-831 in in F x 10-5 3.9 Coefficient of Thermal Conductivity ASTM C-177 BTU hrft2Fin 1.3 Specific Heat Capacity at 77F NA BTU lb F 0.35 Maximum Recommended Continuous Service Temperature NA F 180 200 Recommended Thermoforming Temperature NA F Not recommended Constant Stress Craze Resistance IPA3 Modified ARTC Method Mil P-6997 psi 2100 Constant Stress Craze Resistance Aromatic Alcohol Blend3 Modified ARTC Method Mil P-6997 psi 1700 1.0 THICKNESS 0.118 0.177 0.236 0.354 0.472 0.625 0.708 0.944 SHEET SIZE 48 X 96 49 X 97 50 x 99 51 x 100 60 x 96 61 x 97 62 x 99 63 x 100 72 x 96 73 x 97 74 x 99 75 x 100 Custom lengths are available with minimum requirements. Craze Resistance Flammability2 Specification Compliance ASTM D-635 in min Smoke Density ASTM D-2843 1.0 Self Ignition Temperature ASTM D-1929 F 860 Plastics Component QMFZ2.E39437 Flammability Classification UL 94 94HB 0.060 Plastics Component QMFZ2.E39437 Outdoor Suitability UL 746C f1 0.060 Colorless f2 0.060 ALL International Building Code IBC 2606.4 CC2 0.118 0.944 International Residential Code IRC 308.3 CC2 0.125 American National Standard for Safety Glazing ANSI Z97.1 PASS 0.080 FMVSS 205 Federal Motor Vehicle Safety Glazing FAA FAR Section 25.853 Standard Specification for PMMA Acrylic Plastic Sheet ANSI Z26.1 AS-5 AS-6 AS-7 Appx F Part 1 Paragraphs a1iv Procedure b5 15 second horizontal burn PASS 0.118 0.472 ASTM D-4802 Category A-1 Finish 2 Data given are average values and should not be used for specification purposes. 1. This property will change with thickness. The value given is for the thickness indicated in the column heading unless otherwise noted. 2. Flammability tests are small scale tests and may not be indicative of how
materials will perform in an actual situation. 3. The values are after the material has been heated for forming. Plexiglas acrylic plastic is a combustible thermoplastic. Observe fire precautions appropriate for comparable forms of wood and paper. For building uses check code approvals. Impact resistance is a factor of thickness. Avoid exposure to heat or aromatic solvents. Clean with soap and water. Avoid abrasives. The statements technical information and recommendations contained herein are believed to be accurate as of the date hereof. Since the conditions and methods of use of the product and of the information referred to herein are beyond our control Arkema expressly disclaims any and all liability as to any results obtained or arising from any use of the product or reliance on such information NO WARRANTY OF FITNESS FOR ANY PARTICULAR PURPOSE WARRANTY OF MERCHANTABILITY OR ANY OTHER WARRANTY EXPRESS OR IMPLIED IS MADE CONCERNING THE GOODS DESCRIBED OR THE INFORMATION PROVIDED HEREIN. The information provided herein relates only to the specific product designated and may not be applicable when such product is used in combination with other materials or in any process. The user should thoroughly test any application before commercialization. Nothing contained herein constitutes a license to practice under any patent and it should not be construed as an inducement to infringe any patent and the user is advised to take appropriate steps to be sure that any proposed use of the product will not result in patent infringement. See MSDS for Health Safety Considerations. Altuglas and Plexiglas are registered trademarks of Arkema. 2013 Arkema Inc. All rights reserved. ROC 213 Horizontal Burn Rate1 2
